Piston Skirt Coatings for Alusil and Lokasil Engines: What Matters and Why

Modern aluminum engine blocks such as Alusil and Lokasil rely on exposed silicon crystals within the cylinder wall for wear resistance. Because these bores do not use iron liners, pistons require a ferrous skirt coating to prevent aluminum-on-aluminum contact and galling. Overlooking this detail can turn a healthy engine into a bore-scored core in a hurry, especially without proper maintenance.

Why Ferrous Coatings Are Essential

Without a ferrous barrier on the piston skirt, the aluminum piston can contact the silicon-rich aluminum bore surface. Once that happens, the result is rapid galling and, soon after, bore scoring. Either outcome can force an expensive repair—boring and sleeving the block or replacing it entirely.

Two Proven Approaches: Ferrostan and Ferroprint

Mahle developed two widely used skirt coatings for Alusil/Lokasil applications—both seen in high-performance engines from Porsche, BMW, and Mercedes-Benz. They differ in construction, application method, and long-term durability.

Ferrostan (Electroplated Iron/Tin)

• What it is: A dual-layer electroplated coating—an iron layer for wear resistance topped with a thin tin layer to aid break-in.
• How it’s applied: Electroplating bonds the iron layer metallurgically to the piston skirt.
• Why it matters: The bonded iron layer is extremely hard and durable, offering excellent long-term protection under high load and temperature.
• Trade-offs: Electroplating involves chemicals and processes with environmental considerations; many manufacturers reduced or phased out this method in favor of alternatives.

Ferroprint (Resin with Stainless Particles)

• What it is: A polymer-resin coating infused with stainless steel particles.
• How it’s applied: Typically screen-printed or sprayed onto the skirt, then cured.
• Why it matters: Easier to apply and generally more environmentally friendly from a manufacturing standpoint.
• Trade-offs: While effective within its limits, it does not typically match Ferrostan’s long-term durability in severe service.

Durability and Failure Modes

Historical field experience shows Ferrostan holds up exceptionally well in demanding conditions, with very low incidence of bore scoring when used correctly. Ferroprint offers a cleaner production process and solid performance for many applications, but it is generally considered less durable over extended high-load, high-heat use.

If either coating is damaged during assembly—or simply worn through in service—the aluminum piston skirt can contact the Alusil/Lokasil bore. That metal-to-metal contact accelerates wear, leading first to scuffing and galling, then to visible scoring that compromises sealing and oil control.

Best Practices for Builders and Owners

• Specify the right pistons: Use pistons specifically engineered for Alusil/Lokasil with an appropriate ferrous skirt coating. As of writing this, Mahle Motorsport is the only aftermarket piston manufacturer that offers the required coatings.
• Match use to coating: Ferroprint is not compatible with other cylinder bore technologies, like Nikasil or even cast iron cylinder bores.
• Inspect before assembly: Verify continuous, intact skirt coverage; avoid nicks or handling damage that could become failure initiation sites.
• Use correct clearances: Follow the piston manufacturer’s clearance and finish requirements for Alusil/Lokasil bores.
• Control lubrication and break-in: Proper assembly lube, first-start procedure, and early oil changes reduce risk during the most vulnerable hours of operation.

Bottom Line

In Alusil and Lokasil engines, skirt coating choice is not cosmetic—it is fundamental to reliability. Ferrostan provides the most robust long-term protection, but it's not used anymore; Ferroprint is a viable, cleaner-production alternative when used within its operating limits, requiring the correct bore prep, clearances, and engine oils. Choose wisely, assemble carefully, and you greatly reduce the risk of bore scoring.